Silicon Rubber for pads( SGS.MSDS.ROSH.ISO9001) Rubber series

Features: ( 1) Silicon rubber for pad printing with SGS and ROSH approval ( 2) Curing agent arrange together as free charge
special silicone products for pad printing

Special silicone rubber for pad printing

Model: 918#

Appearance: yellow, red, green, white

Viscosity( cs) : 15000-18000

Hardness( A) : 28-30

Tensile strength ( kgf/ cm) : e35

Elongation break( % ) : e500

Retractility ( % ) : d0.3

Curing agent mixed rate( % ) : 2-3

Operate time( min) : 30

Curing time( hours) : 2-4

Model: 928#

Appearance: translucent

Viscosity( cs) : 15000-18000

Hardness( A) : 28-30

Tensile strength( kgf/ cm2 ) e35

Tear strength ( kgf/ cm) : e20

Elongation break( % ) : e410

Retractility ( % ) : d0.3

Curing agent mixed rate( % ) : 2-3

Operate time( min) : 30

Curing time( hours) : 2-4

Model: 966#

Appearance: white

Viscosity( cs) : 15000-18000

Hardness( A) : 24

Tensile strength( kgf/ cm2 ) e35

Tear strength ( kgf/ cm) : e20

Elongation break( % ) : e410

Retractility ( % ) : d0.3

Curing agent mixed rate( % ) : 2-3

Operate time( min) : 30

Curing time( hours) : 2-4

Model: 900#

Appearance: yellow

Viscosity ( cs) : 18000

Hardness ( A) : 25

Tensile strength( kgf/ cm2 ) e35

Tear strength ( kgf / cm) : e20

Elongation break( % ) : e400

Retractility ( % ) : d0.3

Curing agent mixed rate ( % ) : 2-3

Operate time ( min) : 30

Curing time ( hours) : 2-4

Model: 911#

Appearance: yellow, red, green, white

Viscosity( cs) : 15000-18000

Hardness( A) : 25

Tensile strength( kgf/ cm2 ) e35

Tear strength ( kgf/ cm) : e19

Elongation break( % ) : e400

Retractility ( % ) : d0.3

Curing agent mixed rate( % ) : 2-3

Operate time( min) : 30

Curing time( hours) : 2-4

Model: 912#

Appearance: red, green

Viscosity( cs) : 15000-18000

Hardness( A) : 28-30

Tensile strength ( kgf/ cm) : e33

Elongation break( % ) : e400

Retractility ( % ) : d0.3

Curing agent mixed rate( % ) : 2-3

Operate time( min) : 30

Curing time( hours) : 2-4

Model: 2018#

Appearance: white

Viscosity ( cs) : 12000-15000

Hardness ( A) : 23-26

Tensile strength ( kgf / cm) : e25

Elongation break( % ) : e350

Retractility ( % ) : d0.3

Curing agent mixed rate ( % ) : 2-3

Operate time ( min) : 30

Curing time ( hours) : 2-4

Whatever you have any further information required or suggestion, pls feel free to contact Taylor:
Tel: + 86-755-89948019
Fax: + 86-755-89948030
E-mail: hyw@ szrl.net
MSN: taylordl828@ hotmail.com
Skype: taylordl828
Yahoo: taylordl828@ yahoo.com

Thank you for your attention.