Mold Making Silicone Rubber for Artwork Molds

Mold Making Silicone Rubber Features:
1) High reproduction with reasonable price.
2) Curing agent for free.
3) resistance to deformation and expansion, easy demold
Production mold casting wax, gypsum, concrete or resins ( urethane, polyester, etc. )
( 1) Excellent performance
2) High tear strength
3) Resistance to high temperature
4) Competitive price
5) Samples are available

Description of Mold Making Silicone Rubber
Mold Making Silicone Rubber are generally named as two-part room temperature sulfurated silicone rubber, which features an exceptional fluidity and good operability. When mixed with 2% -3% curing agent, they can still be operated within 30 minutes, but will be formed after 2-3 hours. With resistance to deformation, high temperature, acid and alkali, and expansion

Application of Mold Making Silicone Rubber
RTV-2 silicone rubber is mainly used for toy gifts and craftwork gifts with the advantages of good tensile strength, high tear strength, high temperature resistance, high duplication times and repeated use, etc. RTV-2 silicone rubber is suitable for small products or fine and precision products which is difficult to demould. RTV-2 silicone rubber is one of mold making silicone rubber with the highest use level in the production of craftwork gifts and the shrinkage is up to 0.2%

Special explanation of Mold Making Silicone Rubber
( 1) With SGS and RoHS approval
( 2) Normally Curing agent arrange together as free charged
( 3) In liquid form and in various colors
( 4) With an exceptional fluidity and good operability.
( 5) Temperature and deformation resistance as well as low shrinkage.
( 6) High duplication times.
( 7) Sample are available

Datasheet of Mold Making Silicone Rubber
638# Mainly be used for making various mold which features detailed pattern crafts, plastic, resin products and so on.
Model 638#
Appearance white
Mixing proportion of curing agent( % ) 2
Operating time ( hours ) 0.5
Curing time( hours ) 2-4
Hardness ( shore A) 22-28
Viscosity ( CS) 25000-30000
Tensile-strength( kgf / cm2 ) & ge; 37
Tear-strength ( kgf / cm2 ) & ge; 28
Elongation-break( % ) & ge; 540
Retractility( % ) & le; 0.25
Packing ( kg/ pail ) 25, 200

728# white, the usage for poly crafts, lighting and candles, molds in multiple pieces for large products.
Model 728#
Appearance white
Mixing proportion of curing agent( % ) 2
Operating time ( hours ) 0.5
Curing time( hours ) 2-4
Hardness ( shore A) 25-30
Viscosity ( CS) 25000-28000
Tensile-strength( kgf / cm2 ) & ge; 35
Tear-strength ( kgf / cm2 ) & ge; 25
Elongation-break( % ) & ge; 470
Retractility( % ) & le; 0.25
Packing ( kg/ pail ) 25, 200

788# white, the usage for poly crafts, lighting and candles, multiple piece molds for large product.
Model 788#
Appearance white
Mixing proportion of curing agent( % ) 2
Operating time ( hours ) 0.5
Curing time( hours ) 2-4
Hardness ( shore A) 28-32
Viscosity ( CS) 28000-30000
Tensile-strength ( kgf / cm2 ) & ge; 35
Tear-strength ( kgf / cm2 ) & ge; 20
Elongation-break( % ) & ge; 470
Retractility( % ) & le; 0.3
Packing ( kg/ pail ) 25, 200

Whatever you have any further information required or suggestion, pls feel free to contact

Thank you for your attention.

Taylor
Tel: + 86-755-89948019
Fax: + 86-755-89948030
E-mail: hyw@ szrl.net
MSN: taylordl828@ hotmail.com
Skype: taylordl828
Yahoo: taylordl828@ yahoo.com